Ifomula yepeyinti yokulinganisa i-porcelain ye-putty yodonga lwangaphakathi nangaphandle
Jonga iresiphi engezantsi, kwaye ulungelelanise umlinganiselo ngokweyona meko:
Ngaphakathi eludongeni putty powder:
Ikhalsiyam enzima 800KG (280~320 mesh)
I-Ash calcium 150~200KG (280~320 mesh)
IHydroxypropyl methylcellulose HPMC (100,000 viscosity) 3-5KG
White wood cellulose 3KG (isitatshi etere, eluhlaza esulungekileyo, Pengrun umhlaba, citric acid, polyacrylamide, njl. ingongeza ngokufanelekileyo)
Umgubo weputty wangaphandle:
Isamente 350KG
Ikhalsiyam enzima 500KG
Isanti yequartz 150KG
Redispersible latex powder 8-12KG
IHydroxypropyl Methyl Cellulose 3KG
Isitatshi ether 0.5KG
I-Wood fiber 2KG
Igama leresiphi: ukulinganisa ipeyinti yeporcelain
01. Igama lemathiriyeli ekrwada:
1. I-polyethylene: Iqondo le-alcoholic liyadingeka ukuba libe yi-97%, kwaye i-degree of polymerization yi-1700.
2. I-Quicklime powder: i-quicklime eqhelekileyo.
3. Ukukhanya kwe-calcium carbonate: i-crystal emhlophe okanye i-powder phezu kwe-120 mesh.
4. Umgubo weTalc: ngaphezu kwe-200 mesh emhlophe, umbala okhanyayo okanye otyheli okhanyayo.
5. I-Hydroxypropyl methylcellulose: ukuqina kunye nokugcinwa kwamanzi.
02. Indlela yokupheka: 929, 988
Polyvinyl utywala iglu 100100
Quicklime amanzi 3040
Ukukhanya kwe-calcium carbonate 2015
Umgubo weTalc 3530
Carboxymethyl cellulose ulwelo 3030
03. Inkqubo yokuvelisa:
1. I-Polyvinyl alcohol glue ichithwe ngokupheleleyo kumanzi angama-90-degree: i-carboxymethyl fiber ifakwe emanzini iiyure ezili-12 ngaphambi kokusetyenziswa.
2. Nyibilikisa i-quicklime emanzini ukwenza amanzi ekalika ahluthisiweyo.
3. Xuba kwaye uzulazule ngokulinganayo le mathiriyeli ekrwada ekhankanywe ngasentla.
4. Ngokweendlela ezahlukeneyo zokwakha ezifana nokuxubha, ukukrwela, ukutshiza, ukugquma, njl.njl., ubungakanani beglue ye-polyvinyl alcohol glue kunye ne-carboxymethyl cellulose liquid inokwandiswa ngokufanelekileyo okanye incitshiswe.
Ixesha lokuposa: May-26-2023