Abstract:Ut reponere non-degradable polyvinyl alcohol (PVA) Slurry, cannabis, celluloso aether-hydroxypropyl methylcellosus paratus a agriculturae vastum canny caules et mixta amulum parare slurry. Polyester-bombacio mixtum yarn T / C65 / XXXV 14.7 Tex est amplitudo et ejus sizing perficientur esse probata. Optimal productionem processus hydroxypropyl methylcellosus fuit ut sequitur: Missa fraction de Lye erat XXXV%; et compressio ratio alkali Cellulose erat 2.4; Liquid volumine proportionalis methane et propylene cadmiae est VII: III; Dilute cum Isopropanol; Et reactionem pressura est II. 0PA. Magnitudo paratus a miscentes hydroxypropyl methylcellosus et specifica amulum habet inferioribus cod et magis environmentally amica, et omnia sizing Indicatores potest reponere PVA magnitudine.
Key verba:cannaba; cannabis cellulosa aether; Polyvinyl alcohol; Cellulose aething
0.Praefatio
Sina est unus de terris cum relative dives paleas opibus. In seges output est magis quam DCC decies tons et ad usum rate of paleas est solum III% omni anno. Magna copia paleas non est usus. Paleas est dives naturalis Lignocellulosic rudis materia, quae possunt esse in feed, stercorat, Cellulose derivationes et alia products.
In praesenti, desiderium wastewater pollutio in textile productionem processus facta est maxima pollutio fontes. Et eget oxygeni postulat PVA valde altum. Post Industrial Wastewater produci per PVA in printing et tinctura processus est dimitti in flumen, et inhibere vel etiam perdere respiratio aquatilium organizati. PVA aggravans release et migratio grave metalla in sedimenta in aqua corpora, causando gravius environmental problems. Ad portare investigationis in repositoque PVA cum viridi slurry, necesse est non solum in occursum de requisitis in singing processus, sed etiam ad minimize pollutio aquae et aere in singing processus.
In hoc studio, cannabyl cellulosa aether-hydroxypropyl methylcellosa (HPMC) paratus agriculturae vastum caules et productionem processus dictum. Et miscere hydroxypropyl methylcellulosis et specifica amulum amplitudo quasi magnitudine pro Sizing, compare cum PVA mole, et de ejus sizing perficientur.
I. Experimentum
I. I materiae et instrumenta
Hemp stragulum, Heilongjiang; Polyester-bombacio mixtum yarn T / C65 / 3514.7 Tex; Self-fecit cannabis, cellulosa aether-hydroxypropyl methylcellulosis; -CI, mutatio amulum, PVA-MDCCXCIX, PVA-DLXXXVIII, Liaoning Zhongze Group Chaoyang Textile Co., Ltd.; propanol, premium gradu; Propylene cadmiae, glacial acetic acidum, sodium hydroxide, isopropanol, analytice pura; methyl chloride, summus puritas nitrogen.
GSH, 3L reactionem kettle, JRA-VI Digital Display Magnetic Surgens aqua balneum, DHG-9079A Electric calefacit constant temperatus Machina, Yarg, Ikarw-XX-109b computeriszing tincidunt abrasion-109b unam tincidunt tincidunt abrasion-109b computerized tincidunt, meter.
1.2 Praeparatio hydroxypropyl Methylcellulose
I. II. I Praeparatio Alkali alimentorum fibra
Scinditur in cannabili calamos, conteret ad XX Meshes cum pulverizer, adde cannam strage pulveris ad XXXV% Neoh Aqueous solutio, et inebriat eam ad locus temperatus ad I. V ~ II. 0 h. Exprimendum est imparetur alkali fibra ita ut Missam Ratio Alkali, Cellulose et aqua sit I. II: I. II: I.
I. II. II Etherification reactionem
Projice paratus alkali Cellulose in reactionem olestle, addere C ml of isopropanol ut diluent, addere liquidum CXL ml de methyl chloride et LX ml propylene cadmiae, vacuoize et pressurize ad II. 0 MPA, tardius elevare ad temperatus ad XLV ° C ad 1-2 horas et agere ad LXXV ° C ad 1-2 horas parare hydroxypropyl methylcellose.
I. II. III post processus
Adjust in PH de Etherified Cellulose aether cum glacial acetic acidum ad VI. V ~ VII. V, lavit cum propanol ter, et siccat in clibano ad LXXXV ° c.
1.3 productio processus hydroxypropyl methylcellosa
I. III. I De influentia gyratorius celeritate in praeparatione Cellulose aether
Solet Ehereotheration reactionem est heterogenea reactionem ab intus ad intus. Si non est externum, difficile est inherere agente intrare crystallization cellulis, ita necesse est plene miscere etherification agente cum Cellulose per turbantes. In hoc studio, in altus-pressura Suscitavit Reactor est usus. Postquam iterum experimenta et demonstrationes, lectus gyratorius celeritate erat 240-350 r / min.
I. III. II De effectu Alkali concentration in praeparatione Cellulose aether
Alkali potest perdere de pacto structuram de cellulosose ad eam tumorem, et cum tumor de Amorphous regionem et crystallinum regionem tendunt ad esse consistent, et exherendo procedit blande. In productio processus of Cellulose aether, moles alkali usus est in cellulosose alkalization processus habet magna influentiam in aherification efficientiam etherification products et in gradu substitutione coetus. In praeparatio processus of hydroxypropyl methylcellosus, sicut concentration Lye augetur, contentus de mettofyl coetus etiam crescit; Vice versa, cum concentration de lixa decrescit, hydroxypropyl Methylcellulose in basi contentus est maior. In content of Mthoxy coetus est directe proportionalis ad concentration de lixe; In contentus de hydroxypropyl esse reciproce proportionalem ad concentration Lye. Missam fractionem naoh electus ut XXXV% post iterat probat.
I. III. III De Effectus Alkali Cellulose urgeat Ratio in praeparatione Cellulose aether
Ad pressionem alkali fibra est control aquae contentus de alkali Cellulose. Cum urgeat Ratio est parva, aqua contentus auget, concentratio lixes decrescit, et aeryification rate diminutionem, et exherendum agens est hydrolyzed et latere motus incremento. Et exherendo efficientiam valde reducitur. Cum urgeat Ratio est nimis magna, in aqua contentus decrescit, cellulosa non potest tumidus, et non habet reactivity et inherere non potest plene contactus cum alkali Cellulose et reactionem est inaequale. Post multos probat et urgeat similia, determinatur quod Missam Ratio Alkali, aqua et Cellulose erat I. II: I. II: I.
I. III. IV Effectus temperatus in praeparatio Cellulose aether
In processus of parat hydroxypropyl Methylcellulose, primo temperatus ad 50-60 ° C et custodi illud ad constant temperatus ad II horas. Et hydroxypropylation reactionem potest ferri ex circiter XXX ℃ et hydroxypropylation reactionem rate augetur valde ad L ℃; Tardius levare temperatus ad LXXV ℃ et temperatus ad II horas. In L ° C, in methylation reactionem vix reagit, ad LX ° C, reactionem rate est tardus, et ad LXXV ° C, in methylation Rate Rate est valde accelerated.
Praeparatio Hydroxypropyl Methylcellulose cum multi-scaena temperatus potestate potestate non solum control statera de methtoxyl et hydroxypropyl coetus, sed etiam auxilium redigendum latus reactiones et post-curatio et obtinere products cum rationabile structuram.
I. III. V Effectus Effering agente Dosis Ratio in praeparatione Cellulose aether
Cum hydroxypropyl methylcellose est typical non-Ionic mixto Ather, in methyl et hydroxypropyl coetus substituatur in diversis hydroxypropyl methylcellose Macromolecular vincula, id est diversis C in GLYCOSA circulum. In alia manu, distributio ratio METHYL et hydroxypropyl est maius dispersionem et randomnness. Aquam solubility HPMC est ad contentus de Mthoxy coetus. Cum contentus de methxy coetus humilis, potest dissolvi fortis alkali. Sicut in metxyl contentus crescit, fit magis sensitivo aqua tumor. Altior Mthoxy contentus melius aqua Solubility et potest formari in slurry.
Et moles ethering agente methyl chloride et propylene cadmiae habet recta impulsum in contentus de mettoxyl et hydroxypropyl. Ut parare hydroxypropyl methylcellulose cum aqua solubility, liquidum volumine ratio Methyl chloride et propylene cadmiae electus ut VII: III.
1.3,6 et meliorem productio processus of hydroxypropyl methylcellulosis
Et reactionem apparatu est summus pressura commovit reactor; Rotationis celeritas est 240-350 R / min; Missam fraction de Lye est XXXV%; Et compressionem Ratio de Alkali Cellulose est II. IV; Hydroxypropoxylation ad L ° C II horis, Metxylation ad LXXV ° C II horas; Etherification agente methyl chloride et propylene cadmiae liquidum volumen Ratio VII: III; vacuo; pressura II. 0 MPA; Diluent isopropanol est.
II. Deprehensio et Application
2,1 Sem de Hemp Cellulose et alkali Cellulose
Comparet increatos cellulosa et cannascum cellulosa tractata cum XXXV% Neoh, quod potest esse scilicet quod alkalized cellulosa habet plus superficiem rimas, maior superficies, altior et facilius etherification reactionem.
2.2 infrared spectroscopy determinatio
Cellulose extraxerunt a cannabis stipi post curatio et infrared spectro de HPMC paratus a cannabum stipes cellulosa. Inter eos fortes et wide effusio cohortis ad MMMCCXCV cm -1 est extensio vibrationis effusio cohortis HPMC Association Hydroxyl Group, Effusio Band ad MCCL ~ MCDLX cm -1 est effusio cohortem in aquam ad MDC -1 est effusio cohortem in aquam ad Effationem Band. Et effusio cohortis at 1025cm -1 est effusio cohortem de C - o - c in Polymer.
2.3 Viscositas determinatio
Take paratus Cannabis cellulosose etether sample et addere eam ad compensatur ad parare aque II% aqueum solutio, suscitare eam penitus, metimur eius viscosity et viscosity in III temporibus et metimur et mediocris viscosity in III temporibus et metimur et metimur et in average Viscosity in III temporibus et metimur et mediocris Viscosity ad III temporibus et metimur et metimur et in average Viscosity ad III temporibus et metimur et metimur et in average Viscosity ad III temporibus et metimur et mediocris Viscosity in III temporibus et metimur et metimur et in average Viscosity in III temporibus et metimur et metimur et average Viscosity ad III temporibus et metimur et mediocris Viscosity in III temporibus et metimur et metimur et in average Viscosity in III temporibus et metimur, et metimur et average Viscosity ad III temporibus et metimur et metimur et average Viscosity in III temporibus. Viscositas paratus Cannabis cellulosa etether sample erat XI. VIII mpa · s.
2.4 SIZing Application
2.4.1 slurry configuratione
Et slurry paratus in 1000ml de slurry cum mole fraction of 3.5%, Suscitavit aequaliter cum mixer, et postea in aquam balneum et succenditur ad XCV ° C ad I h. Simul note quod pulpam coctione continens signari bene ne concentration slurry a augendae propter aquam evaporatio.
2.4.2 Slurry formulation PH, miscibility et Cod
Miscere hydroxypropyl methyl cellulosose et specifica amulum mole parare slurry (I # ~ IV #) et comparare cum PVA formula slurry (0 #) ad analyze PG, miscibility et cod. Et polyester-bombacio miscentur yarn T / C65 / 3514.7 Tex est amplitudo in Ess11000 smzing apparatus, et ejus SIZING perficientur est resolved.
Non potest videri, quod homemade cannabis calaminas cellulosa aether et specifica amulum magnitudine III # sunt meliorem mole Formula: XXV% cannaei cellulosis aether, LXV% modified et X% Fs-CI.
Omnes sizing data sunt comparabiles in Sizing notitia de PVA mole, significans quod mixta magnitudinem hydroxypropyl methylcellosus et propria amulum habet bonum sizing perficientur; Et PH sit propius ad neutrum; Hydroxypropyl methylcellosus et specifica amulum in cod (17459.2 mg / l) de specifica amulum mixta mole fuit significantly minus quam ut de PVA magnitudine (26448.0 mg / l) et environmental tutela est bonum.
III. Conclusio
Et meliorem productio processus parat cannabis cellulosose aething-hydroxypropyl Methylcellulose pro SIZing est ut sequitur: A summus pressura Suscitavit REACTOR cum Rotation 240-350 R / Mission est Lye Cellulose 2.4, et MISSIGNATIO Missa est L. ℃ ℃, quisque servetur pro II horis, liquidum volumine Ratio est Methyl chloride et propylene cadmiae est VII: III, vacuum, quod reactionem pressura est 2.0 MPA, isopropanol est diluent.
Hemp cellulosose cellulosis aether est ad reponere PVA mole pro Sizing, et meliorem magnitudinem Ratio fuit: XXV% cannaeum stipes Cellulose aether, LXV% modified amulum et X% II-CI. Et PH de Slurry est 6.5 et Cod (17459.2 mg / l) est significantly inferior, quam quod PVA slurry (26448.0 mg / l), ostendens bonum environmental perficientur.
Hemp cellulosis et aething in sizing pro sizing pro PVA mole ad sizing in polyester-bombacio miscentur yarn T / c LXV / 3514.7TEX. Et sizing index est equivalent. Novum cannabum cellulosa aether et mutatio amulum mixta mole potest reponere PVA mole.