Ngwa ngwa agwakọta akọrọ bụ ụdị granule na ntụ ntụ nke a na-agwakọta ya na ihe mgbakwunye dị ka ezigbo aggregates na inorganic binders, ihe na-ejigide mmiri na ihe na-eme ka mmiri sie ike, ihe ndị na-ebelata mmiri, ihe ndị na-egbochi mgbawa, na ndị na-emebi ụfụfụ n'otu akụkụ mgbe ọ gasịrị. ihicha na nyocha. A na-ebufe ngwakọta ahụ na ebe a na-ewu ihe site na ụgbọ mmiri pụrụ iche ma ọ bụ akpa akwụkwọ na-ekpuchi mmiri, wee gwakọta ya na mmiri. Na mgbakwunye na simenti na ájá, ngwa agha agwakọtara akpọnwụ nke a na-ejikarị eme ihe bụ nke a na-emegharị na polymer ntụ ntụ. N'ihi ọnụ ahịa ya dị elu na mmetụta dị ukwuu na arụmọrụ nke ngwa agha, ọ bụ nlebara anya. Akwụkwọ a na-atụle mmetụta nke ntụ ntụ polymer na-ekesa na njirimara nke ngwa agha.
1 Usoro nnwale
Iji chọpụta mmetụta nke ọdịnaya polymer ntụ ntụ na-ekesa na njirimara nke ngwa agha polymer, e mere ọtụtụ usoro usoro site na usoro ule orthogonal wee nwalee dịka usoro nke "Quality Inspection Standard of Polymer Mortar for External Wall Thermal Insulation" DBJOI- 63-2002. A na-eji ya iji chọpụta mmetụta nke ngwa agha polymer na ike njigide tensile, mkpakọ mkpakọ ike nke isi ihe na ike mkpakọ, ike mgbanwe na mkpakọ-na-fold ruru nke polymer ngwa agha n'onwe ya.
Isi akụrụngwa bụ P-04 2.5 nkịtị silica ciment; RE5044 na R1551Z na-emegharị na redispersible latex ntụ ntụ; 70-140 mesh quartz ájá; ihe mgbakwunye ndị ọzọ.
2 Mmetụta nke ntụ ntụ polymer na-ekesa na njirimara nke ngwa agha polymer
2.1 Njikọ aka na mkpakọ shiee bonding Njirimara
Site na mmụba nke ọdịnaya polymer ntụ ntụ na-ekesa agbasa, ike njigide na-agbakọ na ike njigide shiee ike nke ụrọ polymer na ngwa ngwa ciment mụbara, akụkụ ise ahụ kwalitere n'otu n'otu na mmụba nke ọdịnaya ciment. Ọnụ ọgụgụ dị arọ nke isi ihe ọ bụla dị mkpa nwere ike nyochaa n'ụzọ zuru ezu ogo mmetụta ọdịnaya nke polymer ntụ ntụ na-emegharị na arụmọrụ nke ngwa ngwa ciment. Ike shiee mkpakọ na-egosi usoro uto ahịrị. Ihe na-eme n'ozuzu ya bụ na ike nkekọ tensile na-abawanye site na 0.2 MPa na ike njigide shiee na-abawanye site na 0.45 MPa maka mmụba 1% ọ bụla na ntụ ntụ polymer na-ekesa.
2.2 Mkpakọ / mpịachi Njirimara nke ngwa agha n'onwe ya
Site na mmụba nke ọdịnaya ntụ ntụ polymer redispersible, ike mkpakọ na ike mgbanwe nke ụrọ polymer n'onwe ya belatara, na-egosi na polymer nwere mmetụta na-egbochi hydration nke ciment. A na-egosi mmetụta nke ọdịnaya polymer ntụ ntụ na-ekesa na nchịkọta mkpakọ nke ụrọ polymer n'onwe ya na Figure 4. , na mmụba nke redispersible latex ntụ ntụ ọdịnaya, mkpakọ ruru nke polymer ngwa agha n'onwe ya na-ebelata, na-egosi na polima na-eme ka ike siri ike nke polymer. ngwa agha ahụ. Ọnụ ọgụgụ dị arọ nke isi ihe ọ bụla dị mkpa nwere ike nyochaa n'ụzọ zuru ezu ogo mmetụta nke ọdịnaya polymer ntụ ntụ na-agbasa na arụmọrụ nke ngwa agha polymer n'onwe ya. Site na mmụba nke ọdịnaya polymer ntụ ntụ na-emegharị emegharị, ike mkpakọ, ike mgbanwe na nha indentation na-egosi usoro mbelata nke ahịrị. Maka mmụba ọ bụla 1% nke ntụ ntụ polymer na-ekesa, ike mkpakọ na-ebelata site na 1.21 MPa, ike mgbanwe na-ebelata site na 0.14 MPa, na mkpakọ-na-fold ratio na-ebelata site 0.18. A pụkwara ịhụ na mgbanwe nke ngwa agha na-eme ka ọ dịkwuo mma n'ihi mmụba nke ọnụọgụ polymer na-ekesa.
2.3 Ntụle ọnụọgụ ọnụọgụ nke mmetụta nke nha lime-aja na njirimara nke ngwa agha polymer
N'ime ngwa agha polymer, mmekọrịta dị n'etiti lime-sand ratio na redispersible polymer ntụ ntụ ọdịnaya na-emetụta kpọmkwem arụmọrụ nke ngwa agha, n'ihi ya, ọ dị mkpa na-atụle mmetụta nke lime-aja ruru iche iche. Dị ka usoro nhazi data nke ule orthogonal si dị, a na-eji oke lime-aja dị iche iche mee ihe dị ka ihe na-agbanwe agbanwe, a na-ejikwa ọdịnaya polymer redispersible redispersible eme ihe dị ka ihe na-emekarị ka ọ na-esepụta ọnụọgụ ọnụọgụ nke mmetụta nke ngbanwe nke nzu-aja na-agbanwe na ngwa agha. Enwere ike ịhụ na, Site na mmụba nke nzu-aja, arụmọrụ nke ụrọ polymer na ngwa ngwa ciment na arụ ọrụ nke ụrọ polymer n'onwe ya na-egosi usoro mbelata nke linear. A na-ebelata ike nkekọ ahụ site na 0.12MPa, ike nke na-eme ka ọ bụrụ ihe na-eme ka ọ dị ike na-ebelata site na 0.37MPa, ike mkpakọ nke ụrọ polymer n'onwe ya na-ebelata site na 4.14MPa, ike na-agbanwe agbanwe na-ebelata site na 0.72MPa, na mkpakọ-na-n'ogige atụrụ. Ọnụahịa kasị elu nke 0.270
3 Mmetụta nke redisspersible latex ntụ ntụ nwere f na tensile bonding nke polymer Mortar na EPS foamed polystyrene board Njikọta ụrọ polymer na ngwa ngwa ciment na njikọ nke bọọdụ EPS nke ọkọlọtọ DB JOI-63-2002 tụpụtara na-agbagha.
Nke mbụ chọrọ akwa siri ike nke ụrọ polymer, ebe nke ikpeazụ chọrọ mgbanwe dị elu, ma na-eche na ọrụ mkpuchi mkpuchi nke mpụga kwesịrị ịrapara na mgbidi ndị siri ike na mbadamba EPS na-agbanwe agbanwe, n'otu oge ahụ, ọ dị mkpa iji hụ na ọnụ ahịa ahụ dị. ọ bụghị oke elu. Ya mere, onye odee depụtara mmetụta nke ọdịnaya polymer ntụ ntụ na-agbasasị na njirimara na-agbanwe agbanwe nke ngwa agha polymer iche iji mesie mkpa ọ dị.
3.1 Mmetụta nke ụdị polymer ntụ ntụ na-ekesa na ike nkekọ nke bọọdụ EPS
A na-ahọrọ ntụ ntụ latex na-agbanwe agbanwe site na R5, C1, P23; Ndị Taiwanese D2, D4 2; ụlọ S1, S2 2, ngụkọta nke 7; osisi polystyrene họpụtara Beijing 18kg / EPS osisi. Dị ka ọkọlọtọ DBJ01-63-2002 si dị, e nwere ike ịgbatị bọọdụ EPS ma jikọta ya. Uzuzu latex na-agbanwe agbanwe nwere ike imezu ihe achọrọ nke njigide siri ike ma na-agbanwe agbanwe nke ngwa agha polymer n'otu oge.